Hydraulic Standard Sealing Material TPU Granule

- Good Mechanical Properties
- Hydrolysis Resistant
- Excellent Extrusion Resistance
- Chemical Resistance

INQUIRY

Description
Physical Properties
Applications
Important Note
Recommended
Contact Us

Description

TPU granule(thermoplastic polyurethane elastomer)

High tensile properties
High tear strength
Low compression set
Excellent abrasion resistance

Physical Properties

		Unit	P507	P508	P509	P600	P500	P560	P793S
Hardness	DIN 53505	ShoreA	84±2	93±2	95±2	95±2	95±2	97±2	93±2
Hardness	DIN 53505	ShoreD	33±4	44±4	48±4	48±4	48±4	60±4	44±4
Density	ISO 1183	g/cm3	1.16	1.19	1.2	1.2	1.2	1.22	1.14
modulus	DIN 53504	N/mm2	≥6	≥10	≥12	≥10	≥14	≥15	≥8
300% modulus	DIN 53504	N/mm2	≥12	≥18	≥20	≥18	≥28	≥32	≥15
Tensile strength	DIN 53504	N/mm2	≥32	≥45	≥40	≥48	≥42	≥40	≥40
Elongation at break	DIN 53504	%	≥420	≥420	≥400	≥420	≥350	≥300	≥450
Compression set
70℃/24h 25% def.	ISO 815	%	≤23	≤25	≤23	≤25	≤25	≤35	≤28
100℃/24h 25% def.	ISO 815	%	≤45	≤40	≤35	≤40	≤35	≤45	≤45
Rebound resilience	DIN 53512	%	≥50	≥42	≥45	≥40	≥28	≥30	≥42
Tear strength	ISO 34-1	N/mm2	110	130	130	135	120	165	120
Abrasion	DIN ISO 4649	mm3	≤40	≤40	≤40	≤40	≤40	≤50	≤40
Minimum service temperature		℃	-35	-35	-45	-30	-20	-15	-30
Maximum service temperature		℃	80	100	105	110	110	110	90

Data of other materials are available on request.

Applications

Mostly used for rod seals, piston seals and wipers in standard hydraulics. Due to its outstanding hydrolysis resistant, it can be used for water hydraulic, mining, tunnelling, manufacturing of presses, the use in pure and seawater, HFA and HFB fluids and biologically degradable hydraulic fluids (vegetable oils and synthetic esters) and food articles.

Industrial

Mining

Break Hammer

Pneumatic

Oil Gas Extraction

Hydraulic

Engineering Machinery

Important Note

The values shown above are only valid for material samples prepared for test purposes according to the stated standards. The figures should be regarded as guide values only. Kindly note that the results refer exclusively to the specimens tested. Under certain conditions, the test results established can be affected to a considerable extent by the processing conditions and manufacturing process.

We reserve the right to update this data sheet from time to time if new empirical values are available. Errors and omissions excepted.

PUB October 2020

LEARN MORE FROM FAQ

You will find yourself working in a true partnership that results in an incredibleexperience,and an end product that is the best.

How to quickly select the required materials？
First choose the hardness required, and then look at the dielectric resistance of the material, and finally look at the mechanical properties of the material.
What factors have the greatest influence on the service life of seals？
After many years of application feedback and summary discussion, the failure of seals is mainly caused by the internal heat of the material, the mechanical properties of the material are greatly reduced, and the material is affected by the medium, and is damaged by the medium penetration. In both cases, choosing materials with better dynamic properties and better dielectric resistance can solve the problem.
There are so many materials. What should I choose？
C700 and P600 are standard materials for most sealing applications. Of course, the working temperature is too high or there are some special media need to use more appropriate materials.